1. Thermomechanical treatment:
High-temperature thermomechanical treatment can improve the yield ratio and elastic limit of spiral steel pipe. Improve the comprehensive mechanical properties, fatigue properties, and stress relaxation properties of the spiral steel pipe. Reducing the ductile-brittle transition temperature and temper brittleness of steel has the advantages of a simple process and energy saving. High-temperature thermomechanical treatment has a significant effect on the spiral steel pipe. The specific process is heating temperature 920-950 ℃, hot rolling deformation 10%-30%, air cooling time 10-30 seconds, oil quenching; then ordinary tempering or high-temperature rapid tempering above 400 ℃.
2. Chemical heat treatment in ferrite state:
Chemical heat treatment in the ferrite state, such as nitriding, nitrocarburizing, etc., can significantly improve the surface hardness, wear resistance, corrosion resistance, residual compressive stress, and fatigue life of the spiral steel pipe. The chemical heat treatment temperature is generally between 450 and 600 ° C. The quenched and tempered spiral steel pipe can be combined with chemical heat treatment and tempering. The chemical heat treatment temperature of the precipitation-hardened spiral steel pipe is the same as the precipitation-hardening temperature. With the increasing application of spiral steel pipes, the technical and product diversity requirements of spiral steel pipes are also getting higher and higher.
Post time: Aug-16-2023